Titanium Plate Anode For Seawater Treatment And Water Electrolysis

Name: Titanium Plate Anode For Seawater Treatment And Water Electrolysis
Brand: Changsheng
Price: 100 USD

China Titanium Plate Anode For Seawater Treatment And Water Electrolysis factory

Brand Name : Changsheng

Model Number : ASTM

Certification : ISO 9001;2015

Place of Origin : China

MOQ : 10pc

Price : 100usd/set

Payment Terms : L/C, D/A, D/P, T/T, Western Union, MoneyGram

Supply Ability : 5000T/MONTH

Delivery Time : 10-15days

Packaging Details : packed with export wooden case

Shape : Rod

Substrate : Gr1 titanium ribbon

Coating : Ir-Ta Ru-Ir Coating

Lifetime : Available for 50,100 years

Height : 700mm

Felt Thickness : 0.25~5.0mm

Coating Thickness : 4-6um as your requried

Another Name : DSE(Dimensionally Stable Electrode

Electrode Efficiency : ≥ 90%

Durability : Long-lasting

Wire Diameter : 0.15-0.20mm is commonly used

Pt Coating Thickness : 0.5μm - 15 μm

Conductivity : Good

Length : <=2000mm

Coating Material : Platinum precious metal

Contact Now

Description

Titanium Plate Anode is widely used in various industrial processes such as electroplating, electrolysis, and electrochemical reactions.
Made from high-purity titanium, it offers excellent corrosion resistance, long service life, and high current efficiency. Titanium anodes are suitable for use in both acidic and alkaline environments and can be customised to meet specific current density and dimensional requirements.

Compared with other anode materials, the Titanium Coated Plate Anode provides superior performance and extended lifespan, making it an ideal choice for demanding electrochemical applications.

Titanium Substrate Composition

Grade	N (%)	C (%)	H (%)	Fe (%)	O (%)	Ti (%)
Gr1	0.03	0.08	0.015	0.20	0.18	Balance
Gr2	0.03	0.05	0.015	0.30	0.25	Balance

Regular Coating Types

Coating Type	Thickness (μm)
Platinum	0.5 / 1.0
Mixed Iridium & Platinum	0.5 / 1.0
Mixed Ruthenium & Iridium	6–8
Mixed Iridium & Tantalum	6–8

Key Characteristics

Coating: Mixed Ruthenium and Iridium

Chlorine Evolution Potential: < 1.13 V

Polarizability: ≤ 40 mV

Accelerated Life: ≥ 3000 min (at 1000 A/m²)

Anode Strengthening Weight Loss: ≤ 10 mg

Suitable Environment: Chloride-containing solution, pH ≤ 7

Coating Content & Service Life

Coating Load (g/m²)	Estimated Life (hours)
8	> 6,000
10	> 8,000
12	> 10,000
15	> 12,000
20	> 15,000

Recommended Operating Parameters

Current Density: < 600 A/m²

Operating Temperature: 40–60 °C

Chlorine Concentration: 30–50 g/L

Polarity Reversal: Suitable

Reversal Frequency: Every 2–4 hours

Regular Sizes of Titanium Coated Plate

Size (mm)	Quantity / Set
63.5 × 150	13 pcs
64 × 110	7 pcs
80 × 120	1 pc
30 × 183	7 pcs
80 × 185	7 pcs

Applications

Electroplating: Suitable for gold, silver, copper, and other metal plating.
Chlor-Alkali Production: Used in the manufacture of sodium hydroxide and chlorine.
Desalination: Applied in water desalination systems for salt removal.
Seawater Purification: Used to purify seawater for industrial and potable use.
Cathodic Protection: Protects ships, offshore platforms, and submerged structures from corrosion.
Metal Recovery: Recovers valuable metals from industrial waste streams.
Hydrogen Production: Utilised in electrolysis for hydrogen generation.